Ph.D.awfa abdulrasool evaluation research in the Iraqi Journal of Physics
titled " Enhanced Mechanical Property of acrylic polymer/Graphene/Carbon fibers Hybrid for Water Proof Coating"
In this study, the polymeric plate was expanded by nanomaterials (graphene) and polymer-cut polymer fibres. The mixture of polymeric hybrid coatings was prepared from a mixture (acrylic polymer/graphene/cut green carbon) using the lab-temperature casting method. The nanomaterials mixture was prepared using different proportions 0.25, 0.5, 1, and 2% g and 0.25, 0.5, 1, and 2% Gr/5% CF, and then U prepared in a glass vessel on a magnetic stirrer at laboratory temperature for 2 minutes. One hour. The throat was left for 24 hours at laboratory temperature. The scans produced were performed with 1wt%Gr and 1wt%Gr/CF. Impact strength of acrylic polymer with increasing Gr as weight ratio of Gr and impact strength of acrylic polymer with composites of Gr and Gr & CF combined with Gr at 1 wt. & CF by 5% Content. The tensile strength increases further than that of the acrylic polymer with Gr, Gr & CF composites combined with Gr at 0.5 wt% and CF at 5% wt. The pulling strength of the polymer with Gr and CF was greater than that of the acrylic polymer coating. And acrylic polymer coating with Gr. The pulling strength increases with increasing weight percentage, pest percentage is 2% by weight.